Study on manufacturing materials based on polymethyl methacrylate and application for armored composition for RSI-12M ballistic solid propellant charge
257 viewsDOI:
https://doi.org/10.54939/1859-1043.j.mst.82.2022.127-133Keywords:
Poly methylmetacrylat (PMMA); Armouring composition; Ballistic propellant; Anti-tank guided missile (ATGM).Abstract
This paper presents the manufacturing materials based on polymethyl methacrylate and application for armored composition for RSI-12M ballistic solid propellant charge used in the anti-tank guided missile (ATGM) prototype engine. The research results show that the composition materials have high mechanical properties (tensile strength of 52.1 MPa), well adhesion to the surface of the solid propellant charge (adhesion of 54.5 kG/cm2), dynamic viscosity of 0,515 Pa.s, burning materials produce less soot, low ash content (≈1%), long engine working time (>24 seconds), the average working pressure of 6.4 MPa of the anti-tank rocket prototype engines.
References
[1]. Chu Chiến Hữu. “Nghiên cứu chế tạo vật liệu có độ bền nhiệt, bền cơ lý cao và hàm tro thấp từ cao su nitril”, Tạp chí Hóa học số 55 (1), (2017).
[2]. Trần Ngọc Thanh, Hồ Ngọc Minh. “Biến tính epoxy dùng chế tạo lớp hạn chế bề mặt cháy cho thỏi thuốc phóng keo”. Tạp chí Nghiên cứu KH&CNQS, Số 48, (2017).
[3]. J. P. Agrawal. “Polysiloxane-based inhibition system for double-base rocket propellants”, pp. 1, (1997). DOI: https://doi.org/10.1002/(SICI)1097-4628(19980705)69:1<7::AID-APP2>3.0.CO;2-N
[4]. Кузнецов Е. В. , Прохорова И. П. “Производства полимеров и пластических масс на их основе”, стр. 44.
[5]. Албутова Р. Е. и её партнеры. Патент RU 2283295 C1. “Заливочная композиция для бронирования заряда из баллиститного топлива”, (2006).
[6]. Талалаев А. П. и его партнеры. Патент RU 2164616 C1. “Твердотопливный заряд для ракетного двигателя”, (2009).
[7]. Талалаев А. П. и его партнеры. Патент RU2261240C1. “Oгнеэрозионностойкая заливочная композиция с повышенной деформационной способностью”, (2003).
[8]. Красильников Ф. С. Патент RU2412969C1. “Бронесостав для покрытия заряда твердого ракетного топлива”, (2011).
[9]. Tiêu chuẩn TCVN 4501-2:2014: “Chất dẻo – xác định tính chất kéo – phần 2: điều kiện thử đối với chất dẻo đúc và đùn”.
[10]. Tiêu chuẩn ГОСТ 209-75 của Liên Bang Nga: “Резина и клей. Методы определения прочности связи с металлом при отрыве”.